Polypropylene

HP525J is a medium flow homopolymer with bimodal molecular weight distribution and good clarity intended for BOPP films.
Applications:
High quality packaging film for food, Lamination to other films, Metalizing Film, Medical packaging, Thermoformed food containers
 
Spec:
Melt Flow Rate (230 °C, 2.16kg)           3.0 g/l0min
Density              0.9 g/cm3
Flexural Modulus         1550 MPa
Tensile Strength at Yield          35 MPa
Tensile Elongation at Yield     12 %
Izod Impact Strength (notched) at 23 °C         55 J/m
Rockwell Hardness      105 R Scale
Vicat softening point (ION)     156 °C
H.D.T. (0.46 Mpa)         94 °C
Accelerated oven ageing in air at 150 °C         500 hours
Haze (20µm)    0.5 %